Arc welding is a type of welding process using an electric arc to create heat to melt and join metals. A power supply creates an electric arc between a consumable or non-consumable electrode and the base material using either direct DC or alternating AC currents. Arc welding is a fusion welding process used to join metals.

Difference Between Arc Welding and Gas Welding

Arc welding is a welding process that is used to join metal to metal by using electricity to create enough heat to melt metal, and the melted metals when cool result in a binding of the metals. It is a type of welding that uses a welding power supply to create an electric arc between a metal stick " electrode " and the base material to melt the metals at the point of contact. Arc welders can use either direct DC or alternating AC current, and consumable or non-consumable electrodes.

The welding area is usually protected by some type of shielding gas , vapor, or slag. Arc welding processes may be manual, semi-automatic, or fully automated. First developed in the late part of the 19th century, arc welding became commercially important in shipbuilding during the Second World War.

Today it remains an important process for the fabrication of steel structures and vehicles. To supply the electrical energy necessary for arc welding processes, a number of different power supplies can be used. The most common classification is constant current power supplies and constant voltage power supplies. In arc welding, the voltage is directly related to the length of the arc, and the current is related to the amount of heat input.

Constant current power supplies are most often used for manual welding processes such as gas tungsten arc welding and shielded metal arc welding, because they maintain a relatively constant current even as the voltage varies. This is important because in manual welding, it can be difficult to hold the electrode perfectly steady, and as a result, the arc length and thus voltage tend to fluctuate.

Constant voltage power supplies hold the voltage constant and vary the current, and as a result, are most often used for automated welding processes such as gas metal arc welding, flux cored arc welding, and submerged arc welding. In these processes, arc length is kept constant, since any fluctuation in the distance between the wire and the base material is quickly rectified by a large change in current.

For example, if the wire and the base material get too close, the current will rapidly increase, which in turn causes the heat to increase and the tip of the wire to melt, returning it to its original separation distance. The direction of current used in arc welding also plays an important role in welding. Consumable electrode processes such as shielded metal arc welding and gas metal arc welding generally use direct current, but the electrode can be charged either positively or negatively.

It produces a good bead profile with a higher level of penetration. DC- polarity results in less penetration and a higher electrode melt-off rate. It is sometimes used, for example, on thin sheet metal in an attempt to prevent burn-through. Electrode-negative straight polarity results in faster melt-off of the electrode and, therefore, faster deposition rate. With direct current however, because the electrode only creates the arc and does not provide filler material, a positively charged electrode causes shallow welds, while a negatively charged electrode makes deeper welds.

One disadvantage of AC, the fact that the arc must be re-ignited after every zero crossing, has been addressed with the invention of special power units that produce a square wave pattern instead of the normal sine wave , eliminating low-voltage time after the zero crossings and minimizing the effects of the problem.

Duty cycle is a welding equipment specification which defines the number of minutes, within a minute period, during which a given arc welder can safely be used. One of the most common types of arc welding is shielded metal arc welding SMAW , which is also known as manual metal arc welding MMAW or stick welding.

An electric current is used to strike an arc between the base material and a consumable electrode rod or stick. The electrode rod is made of a material that is compatible with the base material being welded and is covered with a flux that gives off vapors that serve as a shielding gas and provide a layer of slag, both of which protect the weld area from atmospheric contamination.

The electrode core itself acts as filler material, making a separate filler unnecessary. The process is very versatile, requiring little operator training and inexpensive equipment. However, weld times are rather slow, since the consumable electrodes must be frequently replaced and because slag, the residue from the flux, must be chipped away after welding. The versatility of the method makes it popular in a number of applications including repair work and construction. Constant voltage, direct current power source is most commonly used with GMAW, but constant current alternating current are used as well.

With continuously fed filler electrodes, GMAW offers relatively high welding speeds; however the more complicated equipment reduces convenience and versatility in comparison to the SMAW process. Originally developed for welding aluminium and other non-ferrous materials in the s, GMAW was soon economically applied to steels. Today, GMAW is commonly used in industries such as the automobile industry for its quality, versatility and speed.

Because of the need to maintain a stable shroud of shielding gas around the weld site, it can be problematic to use the GMAW process in areas of high air movement such as outdoors. FCAW wire is actually a fine metal tube filled with powdered flux materials.

An externally supplied shielding gas is sometimes used, but often the flux itself is relied upon to generate the necessary protection from the atmosphere. The process is widely used in construction because of its high welding speed and portability.

Submerged arc welding SAW is a high-productivity welding process in which the arc is struck beneath a covering layer of granular flux. This increases arc quality, since contaminants in the atmosphere are blocked by the flux. The slag that forms on the weld generally comes off by itself and, combined with the use of a continuous wire feed, the weld deposition rate is high.

Working conditions are much improved over other arc welding processes since the flux hides the arc and no smoke is produced. The process is commonly used in industry, especially for large products. Especially useful for welding thin materials, this method is characterized by a stable arc and high quality welds, but it requires significant operator skill and can only be accomplished at relatively low speeds.

It can be used on nearly all weldable metals, though it is most often applied to stainless steel and light metals. It is often used when quality welds are extremely important, such as in bicycle , aircraft and marine applications. A related process, plasma arc welding , also uses a tungsten electrode but uses plasma gas to make the arc.

The arc is more concentrated than the GTAW arc, making transverse control more critical and thus generally restricting the technique to a mechanized process. Because of its stable current, the method can be used on a wider range of material thicknesses than can the GTAW process and is much faster. It can be applied to all of the same materials as GTAW except magnesium ; automated welding of stainless steel is one important application of the process.

A variation of the process is plasma cutting , an efficient steel cutting process. Other arc welding processes include atomic hydrogen welding , carbon arc welding, electroslag welding , electrogas welding , and stud arc welding. Some materials, notably high-strength steels, aluminium, and titanium alloys, are susceptible to hydrogen embrittlement.

If the electrodes used for welding contain traces of moisture, the water decomposes in the heat of the arc and the liberated hydrogen enters the lattice of the material, causing its brittleness. Stick electrodes for such materials, with special low-hydrogen coating, are delivered in sealed moisture-proof packaging.

Flux used has to be kept dry as well. Some austenitic stainless steels and nickel -based alloys are prone to intergranular corrosion. Such sensitized steel undergoes corrosion in the areas near the welds where the temperature-time was favorable for forming the carbide. This kind of corrosion is often termed weld decay. Knifeline attack KLA is another kind of corrosion affecting welds, impacting steels stabilized by niobium.

Niobium and niobium carbide dissolves in steel at very high temperatures. At some cooling regimes, niobium carbide does not precipitate, and the steel then behaves like unstabilized steel, forming chromium carbide instead.

This affects only a thin zone several millimeters wide in the very vicinity of the weld, making it difficult to spot and increasing the corrosion speed. The cooling rate after this treatment is not important.

Filler metal electrode material improperly chosen for the environmental conditions can make them corrosion -sensitive as well. There are also issues of galvanic corrosion if the electrode composition is sufficiently dissimilar to the materials welded, or the materials are dissimilar themselves.

Even between different grades of nickel-based stainless steels, corrosion of welded joints can be severe, despite that they rarely undergo galvanic corrosion when mechanically joined. Welding can be a dangerous and unhealthy practice without the proper precautions; however, with the use of new technology and proper protection the risks of injury or death associated with welding can be greatly reduced.

Because many common welding procedures involve an open electric arc or flame, the risk of burns from heat and sparks is significant. To prevent them, welders wear protective clothing in the form of heavy leather gloves and protective long sleeve jackets to avoid exposure to extreme heat, flames, and sparks.

The use of compressed gases and flames in many welding processes also pose an explosion and fire risk; some common precautions include limiting the amount of oxygen in the air and keeping combustible materials away from the workplace.

Exposure to the brightness of the weld area leads to a condition called arc eye in which ultraviolet light causes inflammation of the cornea and can burn the retinas of the eyes. Welding goggles and helmets with dark face plates—much darker than those in sunglasses or oxy-fuel goggles —are worn to prevent this exposure. In recent years, new helmet models have been produced featuring a face plate which automatically self-darkens electronically.

These curtains, made of a polyvinyl chloride plastic film, shield nearby workers from exposure to the UV light from the electric arc. Welders are also often exposed to dangerous gases and particulate matter. Processes like flux-cored arc welding and shielded metal arc welding produce smoke containing particles of various types of oxides. The size of the particles in question tends to influence the toxicity of the fumes, with smaller particles presenting a greater danger.

Additionally, many processes produce various gases most commonly carbon dioxide and ozone , but others as well that can prove dangerous if ventilation is inadequate. Certain welding machines which use a high frequency alternating current component have been found to affect pacemaker operation when within 2 meters of the power unit and 1 meter of the weld site. While examples of forge welding go back to the Bronze Age and the Iron Age , arc welding did not come into practice until much later.

In Humphry Davy discovered the short pulsed electric arcs. Around , A. Strohmenger released in Britain a coated metal electrode which gave a more stable arc. In Russian scientist Vladimir Mitkevich proposed the usage of three-phase electric arc for welding. In , alternating current welding was invented by C. Holslag but did not become popular for another decade. Competing welding processes such as resistance welding and oxyfuel welding were developed during this time as well; [30] but both, especially the latter, faced stiff competition from arc welding especially after metal coverings known as flux for the electrode, to stabilize the arc and shield the base material from impurities, continued to be developed.

During World War I welding started to be used in shipbuilding in Great Britain in place of riveted steel plates. The Americans also became more accepting of the new technology when the process allowed them to repair their ships quickly after a German attack in the New York Harbor at the beginning of the war. During the s, major advances were made in welding technology, including the introduction of automatic welding in which electrode wire was continuously fed.

Shielding gas became a subject receiving much attention as scientists attempted to protect welds from the effects of oxygen and nitrogen in the atmosphere. Porosity and brittleness were the primary problems and the solutions that developed included the use of hydrogen , argon , and helium as welding atmospheres.

This, in conjunction with developments in automatic welding, alternating current, and fluxes fed a major expansion of arc welding during the s and then during World War II. During the middle of the century, many new welding methods were invented. Submerged arc welding was invented in and continues to be popular today.

In a Russian, Konstantin Khrenov successfully implemented the first underwater electric arc welding. Gas tungsten arc welding , after decades of development, was finally perfected in and gas metal arc welding followed in , allowing for fast welding of non- ferrous materials but requiring expensive shielding gases.

MIG and Arc Welding: What's the Difference?

Before - yuck! After - Wow! Special Epoxy applied for extra corrosion protection, an additional coating of a good zinc primer then top coated Bengal White. Nice job Mike! Test your welding knowledge!

Gas Welding Basics, Advantages, Disadvantages and Applications

Everything you need to know about the most commonly used welding technique. To put it simply, gas welding is the process of joining metals using the heat transmitted from the flames. The process involves heating the juncture of two metals to a certain point so that they will melt and fuse. Even though it carries a relatively simple definition, the process of gas welding has many specifics. In this article, we will take an in-depth look into gas welding, its applications, advantages, and methodology.

Arc welding

Sponsored Stories

However, neither is quite the case. Both are individual metal-joining sheet metal techniques within the overall sheet metal fabrication process, but each operation differs slightly. In short, welding is a technique that joins metals by melting the base metal and causing fusion, while brazing joins metals by melting and flowing a filler metal into the joint. In brazing and welding, fabricators add a filler metal into the joint. The filler metal can be aluminum-silicon, brass, bronze, copper, copper-silver, gold-silver , nickel alloy, or silve r. In the welding process, fusion is caused. Fusion is the generic fabrication term for joining together metals of similar compositions and melting points.

Your email address will not be published. Skip to content. Production Engineering. Sharing is Caring : -. Today I am going to tell you about difference between arc welding and gas welding.

The two main types of welding are arc welding and gas welding. Both of these are used for joining together metals depending on the nature of the job. Today, we are going to compare the difference between gas welding and arc welding and which method suits best for what application. To get more information about this, continue reading. It is the process of joining together metals using electricity. To keep it simple, while welding the electricity creates an electric, the arc itself produces high heat that melts base metals with filler wire allowing to fuse them into one solid piece. If you are looking for a new arc welder, you can check out this post.

What is Arc Welding? - Definition and Process Types

Я же объяснил тебе, что он зашифрован. Сьюзан, в свою очередь, удивил ответ шефа. - Но ведь у нас есть ТРАНСТЕКСТ, почему бы его не расшифровать? - Но, увидев выражение лица Стратмора, она поняла, что правила игры изменились.  - О Боже, - проговорила Сьюзан, сообразив, в чем дело, - Цифровая крепость зашифровала самое. Стратмор невесело улыбнулся: - Наконец ты поняла.

Стратмор засмеялся. - Годы тренировки. Ложь была единственным способом избавить тебя от неприятностей. Сьюзан кивнула. - А неприятности немалые.



uses electricity to generate heat used to.


Leon G.

Arc welding is a welding process that is used to join metal to metal by using electricity to create enough heat to melt metal, and the melted metals when cool result in a binding of the metals.


Leave a comment

it’s easy to post a comment

You may use these HTML tags and attributes: <a href="" title=""> <abbr title=""> <acronym title=""> <b> <blockquote cite=""> <cite> <code> <del datetime=""> <em> <i> <q cite=""> <strike> <strong>